Product Information
01SPARKLE SILVET® 880-20-J
SPARKLE SILVET® 880-20-J Aluminum Pigment
SPARKLE SILVET 880-20-J is a medium particle size, bright, SPARKLE SILVER® aluminum pigment produced in pellet form to reduce the potential for generating airborne particles and to improve ease of handling. The pellets are composed of 80% aluminum pigment carried in a 20% aldehyde resin and are produced by a low shear process for easy dispersion. The pigment flake has a cornflake geometry. The particle size distribution range is controlled to produce clean chromatic effects when used with transparent pigments and dyes. This grade will produce bright metallic effects with small grain aesthetics when used alone or with other pigments. SPARKLE SILVET 880-20-J is suitable for use in powder coatings applications.
-Non-leafing
-Aluminum pigment granules
This grade is for use in extrusion metallic powder coating applications.
Composition |
80.0% (+/- 2%) minimum Al flake |
Composition |
20.0% (+/- 2%) minimum carrier |
Particle Size-Microns (Target) |
27.5 |
Specific Gravity |
ca 2.07 |
Resin Binder |
Aldehyde Resin |
Non-Volatile By Weight (Target) |
98.5 minimum by weight |
Coatings Application – Pre-weigh the required amount of granules and cover with preferred solvent. Leave for approximately ten minutes to allow the solvent to penetrate the binder matrix. With gentle stirring, slowly add the resin system, and finally, add solvent until desired viscosity is achieved. It is advisable to pre-mix any resins, micro waxes or additives into a resin system prior to mixing with the aluminum dispersion.
Extruded Powder Application – When using SPARKLE SILVET products for manufacturing powder coatings, care must be taken to maintain the aesthetics of the flake and to allow for safe incorporation. The blending of the SPARKLE SILVET with the powder coating resins should be carried out in a low intensity mixer. If this cannot be accomplished, the SPARKLE SILVET pellets should be added at the very end of a high intensity mixer cycle. The objective of mixing is only to distribute the SPARKLE SILVET throughout the batch and not to reduce the pellets to fine particles. When discharging the batch from the mixer to the extruder, the vessels should be bonded to the same electrical potential to prevent static electricity build up. Single or twin-screw extruders can then be used to provide proper dispersion of the SPARKLE SILVET into the powder coating resin. The metallic blend should be extruded below the curing temperature of the resin and then micronized to the proper size. Excessive shear at any point in this process can cause flakes to become folded or broken, thus creating a large number of smaller flakes. This will result in a reduced reflectivity of the flakes and a graying in color.
Aluminum pigment should be stored in the original shipping container and kept tightly sealed. Store containers in a cool, dry, well-ventilated, and properly rated area. Avoid any conditions that will suspend or float the particles in the air, creating a dust cloud. Avoid all possible sources of ignition. For additional information, please refer to the Safety Data Sheet (SDS) for this product, available from Silberline upon request. An SDS is supplied with all samples of this grade.
All statements, information and data presented herein are believed to be accurate and reliable but are not to be taken as a guarantee, express warranty or implied warranty of merchantability or fitness for a particular purpose, or representation, express or implied, for which seller assumes legal responsibility, and they are offered solely for your consideration, investigation and verification. Statements or suggestions concerning possible use of this product are made without representation or warranty that any such use is free of patent infringement and are not recommendations to infringe on any patent. Copyright 2024 Silberline Manufacturing Co., Inc. All Rights Reserved.